H in 304H refers to high temperature, and high carbon content is the guarantee of high temperature strength. When GB150 requires austenite steel to be used above 525 degrees, the carbon content is not less than 0.04%, and the carbide is the strengthening phase, especially the high temperature strength Better than pure austenite. The higher the carbon content, the worse the corrosion resistance of stainless steel and the easier it is to rust. High temperature performance is better than 304 stainless steel.
Stainless steel sheet and plate
304H stainless sheet and coil specification:
Thickness: 1mm-6mm
Width: 500mm-2500mm(cut according to customer’s request)
Length: 500mm-12000mm or coil
Process: HR, CR
Minimum order: 100kg
304H stainless plate specification:
Thickness: 6mm-200mm
Width: 500mm-4200mm
Length: 500mm-12000mm
Process: Hot Rolled
Minimum order:1 piece
Chemical composition:
ASME SA240 |
Elements % |
||||||||
C |
Mn≤ |
P ≤ |
S ≤ |
Si≤ |
Cr |
Ni |
Mo |
N≤ |
|
304H stainless steel plate |
0.04-0.1 |
2.0 |
0.045 |
0.030 |
0.75 |
18.00-20.00 |
8.00-10.50 |
0.1 |
Stainless steel plate 304H Mechanical Properties:
Tensile Strength, MPa |
Yield Strength, MPa |
Elongation, % |
Hardness, HRB |
515min |
205min |
40 min |
92 max |